找到19项技术成果数据。
找技术 >通过形状记忆棒材制备纳米结构钛镍合金
成熟度:通过小试
技术类型:-
应用行业:制造业
技术简介
项目简介:FIELD: metallurgy.SUBSTANCE: proposed alloy features structure of nanocrystalline grains of B2-phase whereinvolume fraction of 0,1 mcm-size grains and those of shape factor of 2 in mutually perpendicular planes makes at least 90 %. Over 50 % of grains have large angular boundaries misaligned relative to adjacent grains through 15 to 90 degrees. Method of making the bar from said alloy comprises thermomechanical processing including plastic straining and recovery annealing. Intensive plastic straining is made in two steps. At first step, equal-channel angular pressing is made to accumulated strain e≥4. At second step, forge ironing and/or drawing are made. Annealing is carried out either in process and/or after every straining step. Equal-channel angular pressing is performed at 400°C. Forge drawing and ironing are made to total reduction of over 60 % at gradual decrease of temperature to t=450…200 °C, while annealing is performed at t=400…200 °C. EFFECT: higher mechanical and functional properties.项目核心创新点:项目详细用途:预期效益说明:
一种钛镍合金添加少量铝钒均匀布料方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种钛镍合金添加少量铝钒均匀布料方法,冷速大于0.5℃/s时,冷速对全脱碳层深度影响不大,但冷速决定全脱碳层的形貌;冷速较大(5℃/s)的全脱碳层铁素体为等轴铁素体,这些铁素体之间镶嵌着点状的珠光体;而冷速较小(0.5℃/s)的全脱碳层铁素体为长条状,且其生长方向为垂直表面,铁素体之间没有点状的珠光体。在高温段保温一段时间的情况下,α+γ两相区加热对全脱碳层深度的影响很小;在高温段不保温的情况下,α+γ两相区加热产生的全脱碳层会遗留到试样的最终表面,适用于钛镍合金添加少量铝钒均匀布料。
一种钕铁硼磁体离子液体电镀锌镍合金的方法
成熟度:正在研发
技术类型:-
应用行业:制造业
技术简介
一种钕铁硼磁体离子液体电镀锌镍合金的方法是将经镀前处理的钕铁硼磁体作为阴极,锌为阳极,含添加剂的离子液体作为电镀液,在磁力搅拌条件下,控制温度、电流密度和电镀时间对钕铁硼磁体实施电镀锌镍合金工艺,后进行出光、钝化和老化处理。此方法镀液成本低、合成简单、操作温度低,避免了析氢反应,得到的镀层光亮致密,经镀后钝化处理镀层与基体结合牢固,耐腐蚀性好。
一种采用铑镀层的铜表面镀层结构
成熟度:正在研发
技术类型:实用新型
应用行业:制造业
技术简介
本实用新型所述一种采用铑镀层的铜表面镀层结构,包括自下而上设置的铜表面层、预镀镍层、光亮电镀镍层、钯镍合金镀层和铑镀层。预镀镍层与铜表面层相接触,并且预镀镍层位于铜表面层的外侧;光亮电镀镍层与预镀镍层相接触,并且光亮电镀镍层位于预镀镍层的外侧;钯镍合金镀层与光亮电镀镍层相接触,并且钯镍镀层位于光亮电镀镍层的外侧;铑镀层与钯镍合金镀层相接触,并且铑镀层位于钯镍合金镀层的外侧。本实用新型所述一种采用铑镀层的铜表面镀层结构,对铜进行铑电镀可以大大提高镀层的硬度和耐磨性,并赋予铜表面层银白色金属光泽,扩展了铜材质的应用范围。
钇的选择性显色剂对硝基偶氮氯膦在镍合金分析中的应用
成熟度:-
技术类型:-
应用行业:科学研究和技术服务业
技术简介
新型测温材料镍铬-镍硅热电偶和镍基汽车火花塞材料是测温仪表和汽车发动机用的关键材料,其中加入轻稀土元素和钇则可大大提高材料抗氧化性及改善材料的性能。但由于轻稀土和钇的化学性质极为相似,其不经分离直接测定是分析化学领域中长期未解决的问题。该校研制的新稀土显色剂-对硝基偶氮氯膦试剂与钇特征β型反应解决了镍合金中钇和铈组共存时钇的测定问题。这一技术为解决镍、铬热电偶代替昂贵的铂铑热电偶创造了条件。该项成果还可扩大应用于高温合金、钢铁、稀土矿石及钢合金等材料中钇和铈组元素的测定。
高钼、钴、镍合金的综合回收
成熟度:-
技术类型:-
应用行业:制造业
技术简介
该成果是利用该所现有设备,在大量试验的基础上研制的。工艺的关键:试料采用一次氧化焙烧,二次苏打焙烧的生产流程,有效地解决了钼与钴、镍的分离。通过控制最佳工艺条件,不仅有价的回收率高,而且产品质量稳定,生产成本低,产品可全部出口,市场前景乐观。该工艺流程短,设备少,环保措施完善,具有明显的经济效益和社会效益。
一种用于锰钒镍合金钢的正火工艺
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种用于锰钒镍合金钢的正火工艺,属于金属热处理技术领域。将根据钢板的厚度进行分组,不同组别的钢板,采用不同的正火工艺,从而使得不同厚度钢板的强度均能满足标准要求。该钢种成分为C≤0.20%,Mn≤1.70%,Si=0.10%~0.50%,V=0.10%~0.18%,Ni=0.40%~0.70%,P≤0.035%,S≤0.035%,其余为Fe和不可避免残余元素。将厚度≤75mm的钢板分为五组,根据不同的分组,采用不同的正火温度和不同的在炉时间。优点在于,工艺简单易行;不同厚度的钢板,其强度均满足标准要求,同时可以避免不必要的能源浪费。
一种镍合金200um涂层的制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
摘要:本发明公开了一种镍合金200um涂层的制备方法,首先对工件表面进行热处理,然后取各种金属粉按比例配置合金粉并搅拌均匀,最后采用等离子喷涂的方法在工件表面喷涂一层合金层。其优点在于:方法简单,原料易得,综合性能好,应用广泛。
一种镍合金基体表面热障涂层及制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种镍合金基体表面热障涂层(专利号201110347751.7),包括微晶玻璃粘结层和陶瓷表层,所述微晶玻璃粘结层及所述陶瓷表层分别由微晶玻璃粉末及稀土锆酸盐粉末通过料浆喷涂沉积在镍合金基体表面。本发明采用与基体有着良好结合的微晶玻璃作为粘结层,可有效提高涂层的抗热震性能;以稀土锆酸盐为表层材料,使涂层具有更好的隔热和抗氧化性能。通过调整料浆喷涂工艺参数可以方便的调整涂层的厚度,以使涂层的强度与厚度达到良好的比例,适应不同的服役环境条件。本发明工艺方法简单,操作简便,制备的涂层具有良好的抗热震性能、隔热和抗氧化性能,可大幅降低生产成本,适用于现代航空发动机、航天器和火箭发动机以及舰艇和工业燃气轮机的关键热端部件的表面处理。
一种铜粉表面包覆磷镍合金层的超声化学制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
本发明涉及金属包覆型复合粉末,特指一种铜粉表面包覆磷镍合金层的超声化学制备方法。该方法的特点是在传统化学镀的工艺中有效的加入了高能超声搅拌,利用其的空穴效应、震荡等效应,提高了镍包覆铜复合粉末制备效率,解决了粉末团聚等问题。另外本发明在制备镍磷包覆型铜粉时,使用次亚磷酸钠作还原剂的酸性化学镀镀液,镀液配制简单,稳定性强,镀覆前的铜粉使用盐酸进行活化处理,克服了传统的铜粉表面要经过贵金属盐活化敏化处理时贵金属钯盐带入镀液导致镀液分解的问题,又简化了粉末的活化工序,同时在整个镀覆的过程中保持高能超声搅拌,制得的复合粉末分散性极好,包覆层完整均匀,镀层致密,呈非晶态。
找到19项技术成果数据。
找技术 >通过形状记忆棒材制备纳米结构钛镍合金
成熟度:通过小试
技术类型:-
应用行业:制造业
技术简介
项目简介:FIELD: metallurgy.SUBSTANCE: proposed alloy features structure of nanocrystalline grains of B2-phase whereinvolume fraction of 0,1 mcm-size grains and those of shape factor of 2 in mutually perpendicular planes makes at least 90 %. Over 50 % of grains have large angular boundaries misaligned relative to adjacent grains through 15 to 90 degrees. Method of making the bar from said alloy comprises thermomechanical processing including plastic straining and recovery annealing. Intensive plastic straining is made in two steps. At first step, equal-channel angular pressing is made to accumulated strain e≥4. At second step, forge ironing and/or drawing are made. Annealing is carried out either in process and/or after every straining step. Equal-channel angular pressing is performed at 400°C. Forge drawing and ironing are made to total reduction of over 60 % at gradual decrease of temperature to t=450…200 °C, while annealing is performed at t=400…200 °C. EFFECT: higher mechanical and functional properties.项目核心创新点:项目详细用途:预期效益说明:
一种钛镍合金添加少量铝钒均匀布料方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种钛镍合金添加少量铝钒均匀布料方法,冷速大于0.5℃/s时,冷速对全脱碳层深度影响不大,但冷速决定全脱碳层的形貌;冷速较大(5℃/s)的全脱碳层铁素体为等轴铁素体,这些铁素体之间镶嵌着点状的珠光体;而冷速较小(0.5℃/s)的全脱碳层铁素体为长条状,且其生长方向为垂直表面,铁素体之间没有点状的珠光体。在高温段保温一段时间的情况下,α+γ两相区加热对全脱碳层深度的影响很小;在高温段不保温的情况下,α+γ两相区加热产生的全脱碳层会遗留到试样的最终表面,适用于钛镍合金添加少量铝钒均匀布料。
一种钕铁硼磁体离子液体电镀锌镍合金的方法
成熟度:正在研发
技术类型:-
应用行业:制造业
技术简介
一种钕铁硼磁体离子液体电镀锌镍合金的方法是将经镀前处理的钕铁硼磁体作为阴极,锌为阳极,含添加剂的离子液体作为电镀液,在磁力搅拌条件下,控制温度、电流密度和电镀时间对钕铁硼磁体实施电镀锌镍合金工艺,后进行出光、钝化和老化处理。此方法镀液成本低、合成简单、操作温度低,避免了析氢反应,得到的镀层光亮致密,经镀后钝化处理镀层与基体结合牢固,耐腐蚀性好。
一种采用铑镀层的铜表面镀层结构
成熟度:正在研发
技术类型:实用新型
应用行业:制造业
技术简介
本实用新型所述一种采用铑镀层的铜表面镀层结构,包括自下而上设置的铜表面层、预镀镍层、光亮电镀镍层、钯镍合金镀层和铑镀层。预镀镍层与铜表面层相接触,并且预镀镍层位于铜表面层的外侧;光亮电镀镍层与预镀镍层相接触,并且光亮电镀镍层位于预镀镍层的外侧;钯镍合金镀层与光亮电镀镍层相接触,并且钯镍镀层位于光亮电镀镍层的外侧;铑镀层与钯镍合金镀层相接触,并且铑镀层位于钯镍合金镀层的外侧。本实用新型所述一种采用铑镀层的铜表面镀层结构,对铜进行铑电镀可以大大提高镀层的硬度和耐磨性,并赋予铜表面层银白色金属光泽,扩展了铜材质的应用范围。
钇的选择性显色剂对硝基偶氮氯膦在镍合金分析中的应用
成熟度:-
技术类型:-
应用行业:科学研究和技术服务业
技术简介
新型测温材料镍铬-镍硅热电偶和镍基汽车火花塞材料是测温仪表和汽车发动机用的关键材料,其中加入轻稀土元素和钇则可大大提高材料抗氧化性及改善材料的性能。但由于轻稀土和钇的化学性质极为相似,其不经分离直接测定是分析化学领域中长期未解决的问题。该校研制的新稀土显色剂-对硝基偶氮氯膦试剂与钇特征β型反应解决了镍合金中钇和铈组共存时钇的测定问题。这一技术为解决镍、铬热电偶代替昂贵的铂铑热电偶创造了条件。该项成果还可扩大应用于高温合金、钢铁、稀土矿石及钢合金等材料中钇和铈组元素的测定。
高钼、钴、镍合金的综合回收
成熟度:-
技术类型:-
应用行业:制造业
技术简介
该成果是利用该所现有设备,在大量试验的基础上研制的。工艺的关键:试料采用一次氧化焙烧,二次苏打焙烧的生产流程,有效地解决了钼与钴、镍的分离。通过控制最佳工艺条件,不仅有价的回收率高,而且产品质量稳定,生产成本低,产品可全部出口,市场前景乐观。该工艺流程短,设备少,环保措施完善,具有明显的经济效益和社会效益。
一种用于锰钒镍合金钢的正火工艺
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种用于锰钒镍合金钢的正火工艺,属于金属热处理技术领域。将根据钢板的厚度进行分组,不同组别的钢板,采用不同的正火工艺,从而使得不同厚度钢板的强度均能满足标准要求。该钢种成分为C≤0.20%,Mn≤1.70%,Si=0.10%~0.50%,V=0.10%~0.18%,Ni=0.40%~0.70%,P≤0.035%,S≤0.035%,其余为Fe和不可避免残余元素。将厚度≤75mm的钢板分为五组,根据不同的分组,采用不同的正火温度和不同的在炉时间。优点在于,工艺简单易行;不同厚度的钢板,其强度均满足标准要求,同时可以避免不必要的能源浪费。
一种镍合金200um涂层的制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
摘要:本发明公开了一种镍合金200um涂层的制备方法,首先对工件表面进行热处理,然后取各种金属粉按比例配置合金粉并搅拌均匀,最后采用等离子喷涂的方法在工件表面喷涂一层合金层。其优点在于:方法简单,原料易得,综合性能好,应用广泛。
一种镍合金基体表面热障涂层及制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种镍合金基体表面热障涂层(专利号201110347751.7),包括微晶玻璃粘结层和陶瓷表层,所述微晶玻璃粘结层及所述陶瓷表层分别由微晶玻璃粉末及稀土锆酸盐粉末通过料浆喷涂沉积在镍合金基体表面。本发明采用与基体有着良好结合的微晶玻璃作为粘结层,可有效提高涂层的抗热震性能;以稀土锆酸盐为表层材料,使涂层具有更好的隔热和抗氧化性能。通过调整料浆喷涂工艺参数可以方便的调整涂层的厚度,以使涂层的强度与厚度达到良好的比例,适应不同的服役环境条件。本发明工艺方法简单,操作简便,制备的涂层具有良好的抗热震性能、隔热和抗氧化性能,可大幅降低生产成本,适用于现代航空发动机、航天器和火箭发动机以及舰艇和工业燃气轮机的关键热端部件的表面处理。
一种铜粉表面包覆磷镍合金层的超声化学制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
本发明涉及金属包覆型复合粉末,特指一种铜粉表面包覆磷镍合金层的超声化学制备方法。该方法的特点是在传统化学镀的工艺中有效的加入了高能超声搅拌,利用其的空穴效应、震荡等效应,提高了镍包覆铜复合粉末制备效率,解决了粉末团聚等问题。另外本发明在制备镍磷包覆型铜粉时,使用次亚磷酸钠作还原剂的酸性化学镀镀液,镀液配制简单,稳定性强,镀覆前的铜粉使用盐酸进行活化处理,克服了传统的铜粉表面要经过贵金属盐活化敏化处理时贵金属钯盐带入镀液导致镀液分解的问题,又简化了粉末的活化工序,同时在整个镀覆的过程中保持高能超声搅拌,制得的复合粉末分散性极好,包覆层完整均匀,镀层致密,呈非晶态。
找到19项技术成果数据。
找技术 >通过形状记忆棒材制备纳米结构钛镍合金
成熟度:通过小试
技术类型:-
应用行业:制造业
技术简介
项目简介:FIELD: metallurgy.SUBSTANCE: proposed alloy features structure of nanocrystalline grains of B2-phase whereinvolume fraction of 0,1 mcm-size grains and those of shape factor of 2 in mutually perpendicular planes makes at least 90 %. Over 50 % of grains have large angular boundaries misaligned relative to adjacent grains through 15 to 90 degrees. Method of making the bar from said alloy comprises thermomechanical processing including plastic straining and recovery annealing. Intensive plastic straining is made in two steps. At first step, equal-channel angular pressing is made to accumulated strain e≥4. At second step, forge ironing and/or drawing are made. Annealing is carried out either in process and/or after every straining step. Equal-channel angular pressing is performed at 400°C. Forge drawing and ironing are made to total reduction of over 60 % at gradual decrease of temperature to t=450…200 °C, while annealing is performed at t=400…200 °C. EFFECT: higher mechanical and functional properties.项目核心创新点:项目详细用途:预期效益说明:
一种钛镍合金添加少量铝钒均匀布料方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种钛镍合金添加少量铝钒均匀布料方法,冷速大于0.5℃/s时,冷速对全脱碳层深度影响不大,但冷速决定全脱碳层的形貌;冷速较大(5℃/s)的全脱碳层铁素体为等轴铁素体,这些铁素体之间镶嵌着点状的珠光体;而冷速较小(0.5℃/s)的全脱碳层铁素体为长条状,且其生长方向为垂直表面,铁素体之间没有点状的珠光体。在高温段保温一段时间的情况下,α+γ两相区加热对全脱碳层深度的影响很小;在高温段不保温的情况下,α+γ两相区加热产生的全脱碳层会遗留到试样的最终表面,适用于钛镍合金添加少量铝钒均匀布料。
一种钕铁硼磁体离子液体电镀锌镍合金的方法
成熟度:正在研发
技术类型:-
应用行业:制造业
技术简介
一种钕铁硼磁体离子液体电镀锌镍合金的方法是将经镀前处理的钕铁硼磁体作为阴极,锌为阳极,含添加剂的离子液体作为电镀液,在磁力搅拌条件下,控制温度、电流密度和电镀时间对钕铁硼磁体实施电镀锌镍合金工艺,后进行出光、钝化和老化处理。此方法镀液成本低、合成简单、操作温度低,避免了析氢反应,得到的镀层光亮致密,经镀后钝化处理镀层与基体结合牢固,耐腐蚀性好。
一种采用铑镀层的铜表面镀层结构
成熟度:正在研发
技术类型:实用新型
应用行业:制造业
技术简介
本实用新型所述一种采用铑镀层的铜表面镀层结构,包括自下而上设置的铜表面层、预镀镍层、光亮电镀镍层、钯镍合金镀层和铑镀层。预镀镍层与铜表面层相接触,并且预镀镍层位于铜表面层的外侧;光亮电镀镍层与预镀镍层相接触,并且光亮电镀镍层位于预镀镍层的外侧;钯镍合金镀层与光亮电镀镍层相接触,并且钯镍镀层位于光亮电镀镍层的外侧;铑镀层与钯镍合金镀层相接触,并且铑镀层位于钯镍合金镀层的外侧。本实用新型所述一种采用铑镀层的铜表面镀层结构,对铜进行铑电镀可以大大提高镀层的硬度和耐磨性,并赋予铜表面层银白色金属光泽,扩展了铜材质的应用范围。
钇的选择性显色剂对硝基偶氮氯膦在镍合金分析中的应用
成熟度:-
技术类型:-
应用行业:科学研究和技术服务业
技术简介
新型测温材料镍铬-镍硅热电偶和镍基汽车火花塞材料是测温仪表和汽车发动机用的关键材料,其中加入轻稀土元素和钇则可大大提高材料抗氧化性及改善材料的性能。但由于轻稀土和钇的化学性质极为相似,其不经分离直接测定是分析化学领域中长期未解决的问题。该校研制的新稀土显色剂-对硝基偶氮氯膦试剂与钇特征β型反应解决了镍合金中钇和铈组共存时钇的测定问题。这一技术为解决镍、铬热电偶代替昂贵的铂铑热电偶创造了条件。该项成果还可扩大应用于高温合金、钢铁、稀土矿石及钢合金等材料中钇和铈组元素的测定。
高钼、钴、镍合金的综合回收
成熟度:-
技术类型:-
应用行业:制造业
技术简介
该成果是利用该所现有设备,在大量试验的基础上研制的。工艺的关键:试料采用一次氧化焙烧,二次苏打焙烧的生产流程,有效地解决了钼与钴、镍的分离。通过控制最佳工艺条件,不仅有价的回收率高,而且产品质量稳定,生产成本低,产品可全部出口,市场前景乐观。该工艺流程短,设备少,环保措施完善,具有明显的经济效益和社会效益。
一种用于锰钒镍合金钢的正火工艺
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种用于锰钒镍合金钢的正火工艺,属于金属热处理技术领域。将根据钢板的厚度进行分组,不同组别的钢板,采用不同的正火工艺,从而使得不同厚度钢板的强度均能满足标准要求。该钢种成分为C≤0.20%,Mn≤1.70%,Si=0.10%~0.50%,V=0.10%~0.18%,Ni=0.40%~0.70%,P≤0.035%,S≤0.035%,其余为Fe和不可避免残余元素。将厚度≤75mm的钢板分为五组,根据不同的分组,采用不同的正火温度和不同的在炉时间。优点在于,工艺简单易行;不同厚度的钢板,其强度均满足标准要求,同时可以避免不必要的能源浪费。
一种镍合金200um涂层的制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
摘要:本发明公开了一种镍合金200um涂层的制备方法,首先对工件表面进行热处理,然后取各种金属粉按比例配置合金粉并搅拌均匀,最后采用等离子喷涂的方法在工件表面喷涂一层合金层。其优点在于:方法简单,原料易得,综合性能好,应用广泛。
一种镍合金基体表面热障涂层及制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种镍合金基体表面热障涂层(专利号201110347751.7),包括微晶玻璃粘结层和陶瓷表层,所述微晶玻璃粘结层及所述陶瓷表层分别由微晶玻璃粉末及稀土锆酸盐粉末通过料浆喷涂沉积在镍合金基体表面。本发明采用与基体有着良好结合的微晶玻璃作为粘结层,可有效提高涂层的抗热震性能;以稀土锆酸盐为表层材料,使涂层具有更好的隔热和抗氧化性能。通过调整料浆喷涂工艺参数可以方便的调整涂层的厚度,以使涂层的强度与厚度达到良好的比例,适应不同的服役环境条件。本发明工艺方法简单,操作简便,制备的涂层具有良好的抗热震性能、隔热和抗氧化性能,可大幅降低生产成本,适用于现代航空发动机、航天器和火箭发动机以及舰艇和工业燃气轮机的关键热端部件的表面处理。
一种铜粉表面包覆磷镍合金层的超声化学制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
本发明涉及金属包覆型复合粉末,特指一种铜粉表面包覆磷镍合金层的超声化学制备方法。该方法的特点是在传统化学镀的工艺中有效的加入了高能超声搅拌,利用其的空穴效应、震荡等效应,提高了镍包覆铜复合粉末制备效率,解决了粉末团聚等问题。另外本发明在制备镍磷包覆型铜粉时,使用次亚磷酸钠作还原剂的酸性化学镀镀液,镀液配制简单,稳定性强,镀覆前的铜粉使用盐酸进行活化处理,克服了传统的铜粉表面要经过贵金属盐活化敏化处理时贵金属钯盐带入镀液导致镀液分解的问题,又简化了粉末的活化工序,同时在整个镀覆的过程中保持高能超声搅拌,制得的复合粉末分散性极好,包覆层完整均匀,镀层致密,呈非晶态。
找到19项技术成果数据。
找技术 >通过形状记忆棒材制备纳米结构钛镍合金
成熟度:通过小试
技术类型:-
应用行业:制造业
技术简介
项目简介:FIELD: metallurgy.SUBSTANCE: proposed alloy features structure of nanocrystalline grains of B2-phase whereinvolume fraction of 0,1 mcm-size grains and those of shape factor of 2 in mutually perpendicular planes makes at least 90 %. Over 50 % of grains have large angular boundaries misaligned relative to adjacent grains through 15 to 90 degrees. Method of making the bar from said alloy comprises thermomechanical processing including plastic straining and recovery annealing. Intensive plastic straining is made in two steps. At first step, equal-channel angular pressing is made to accumulated strain e≥4. At second step, forge ironing and/or drawing are made. Annealing is carried out either in process and/or after every straining step. Equal-channel angular pressing is performed at 400°C. Forge drawing and ironing are made to total reduction of over 60 % at gradual decrease of temperature to t=450…200 °C, while annealing is performed at t=400…200 °C. EFFECT: higher mechanical and functional properties.项目核心创新点:项目详细用途:预期效益说明:
一种钛镍合金添加少量铝钒均匀布料方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种钛镍合金添加少量铝钒均匀布料方法,冷速大于0.5℃/s时,冷速对全脱碳层深度影响不大,但冷速决定全脱碳层的形貌;冷速较大(5℃/s)的全脱碳层铁素体为等轴铁素体,这些铁素体之间镶嵌着点状的珠光体;而冷速较小(0.5℃/s)的全脱碳层铁素体为长条状,且其生长方向为垂直表面,铁素体之间没有点状的珠光体。在高温段保温一段时间的情况下,α+γ两相区加热对全脱碳层深度的影响很小;在高温段不保温的情况下,α+γ两相区加热产生的全脱碳层会遗留到试样的最终表面,适用于钛镍合金添加少量铝钒均匀布料。
一种钕铁硼磁体离子液体电镀锌镍合金的方法
成熟度:正在研发
技术类型:-
应用行业:制造业
技术简介
一种钕铁硼磁体离子液体电镀锌镍合金的方法是将经镀前处理的钕铁硼磁体作为阴极,锌为阳极,含添加剂的离子液体作为电镀液,在磁力搅拌条件下,控制温度、电流密度和电镀时间对钕铁硼磁体实施电镀锌镍合金工艺,后进行出光、钝化和老化处理。此方法镀液成本低、合成简单、操作温度低,避免了析氢反应,得到的镀层光亮致密,经镀后钝化处理镀层与基体结合牢固,耐腐蚀性好。
一种采用铑镀层的铜表面镀层结构
成熟度:正在研发
技术类型:实用新型
应用行业:制造业
技术简介
本实用新型所述一种采用铑镀层的铜表面镀层结构,包括自下而上设置的铜表面层、预镀镍层、光亮电镀镍层、钯镍合金镀层和铑镀层。预镀镍层与铜表面层相接触,并且预镀镍层位于铜表面层的外侧;光亮电镀镍层与预镀镍层相接触,并且光亮电镀镍层位于预镀镍层的外侧;钯镍合金镀层与光亮电镀镍层相接触,并且钯镍镀层位于光亮电镀镍层的外侧;铑镀层与钯镍合金镀层相接触,并且铑镀层位于钯镍合金镀层的外侧。本实用新型所述一种采用铑镀层的铜表面镀层结构,对铜进行铑电镀可以大大提高镀层的硬度和耐磨性,并赋予铜表面层银白色金属光泽,扩展了铜材质的应用范围。
钇的选择性显色剂对硝基偶氮氯膦在镍合金分析中的应用
成熟度:-
技术类型:-
应用行业:科学研究和技术服务业
技术简介
新型测温材料镍铬-镍硅热电偶和镍基汽车火花塞材料是测温仪表和汽车发动机用的关键材料,其中加入轻稀土元素和钇则可大大提高材料抗氧化性及改善材料的性能。但由于轻稀土和钇的化学性质极为相似,其不经分离直接测定是分析化学领域中长期未解决的问题。该校研制的新稀土显色剂-对硝基偶氮氯膦试剂与钇特征β型反应解决了镍合金中钇和铈组共存时钇的测定问题。这一技术为解决镍、铬热电偶代替昂贵的铂铑热电偶创造了条件。该项成果还可扩大应用于高温合金、钢铁、稀土矿石及钢合金等材料中钇和铈组元素的测定。
高钼、钴、镍合金的综合回收
成熟度:-
技术类型:-
应用行业:制造业
技术简介
该成果是利用该所现有设备,在大量试验的基础上研制的。工艺的关键:试料采用一次氧化焙烧,二次苏打焙烧的生产流程,有效地解决了钼与钴、镍的分离。通过控制最佳工艺条件,不仅有价的回收率高,而且产品质量稳定,生产成本低,产品可全部出口,市场前景乐观。该工艺流程短,设备少,环保措施完善,具有明显的经济效益和社会效益。
一种用于锰钒镍合金钢的正火工艺
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种用于锰钒镍合金钢的正火工艺,属于金属热处理技术领域。将根据钢板的厚度进行分组,不同组别的钢板,采用不同的正火工艺,从而使得不同厚度钢板的强度均能满足标准要求。该钢种成分为C≤0.20%,Mn≤1.70%,Si=0.10%~0.50%,V=0.10%~0.18%,Ni=0.40%~0.70%,P≤0.035%,S≤0.035%,其余为Fe和不可避免残余元素。将厚度≤75mm的钢板分为五组,根据不同的分组,采用不同的正火温度和不同的在炉时间。优点在于,工艺简单易行;不同厚度的钢板,其强度均满足标准要求,同时可以避免不必要的能源浪费。
一种镍合金200um涂层的制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
摘要:本发明公开了一种镍合金200um涂层的制备方法,首先对工件表面进行热处理,然后取各种金属粉按比例配置合金粉并搅拌均匀,最后采用等离子喷涂的方法在工件表面喷涂一层合金层。其优点在于:方法简单,原料易得,综合性能好,应用广泛。
一种镍合金基体表面热障涂层及制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种镍合金基体表面热障涂层(专利号201110347751.7),包括微晶玻璃粘结层和陶瓷表层,所述微晶玻璃粘结层及所述陶瓷表层分别由微晶玻璃粉末及稀土锆酸盐粉末通过料浆喷涂沉积在镍合金基体表面。本发明采用与基体有着良好结合的微晶玻璃作为粘结层,可有效提高涂层的抗热震性能;以稀土锆酸盐为表层材料,使涂层具有更好的隔热和抗氧化性能。通过调整料浆喷涂工艺参数可以方便的调整涂层的厚度,以使涂层的强度与厚度达到良好的比例,适应不同的服役环境条件。本发明工艺方法简单,操作简便,制备的涂层具有良好的抗热震性能、隔热和抗氧化性能,可大幅降低生产成本,适用于现代航空发动机、航天器和火箭发动机以及舰艇和工业燃气轮机的关键热端部件的表面处理。
一种铜粉表面包覆磷镍合金层的超声化学制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
本发明涉及金属包覆型复合粉末,特指一种铜粉表面包覆磷镍合金层的超声化学制备方法。该方法的特点是在传统化学镀的工艺中有效的加入了高能超声搅拌,利用其的空穴效应、震荡等效应,提高了镍包覆铜复合粉末制备效率,解决了粉末团聚等问题。另外本发明在制备镍磷包覆型铜粉时,使用次亚磷酸钠作还原剂的酸性化学镀镀液,镀液配制简单,稳定性强,镀覆前的铜粉使用盐酸进行活化处理,克服了传统的铜粉表面要经过贵金属盐活化敏化处理时贵金属钯盐带入镀液导致镀液分解的问题,又简化了粉末的活化工序,同时在整个镀覆的过程中保持高能超声搅拌,制得的复合粉末分散性极好,包覆层完整均匀,镀层致密,呈非晶态。
找到19项技术成果数据。
找技术 >通过形状记忆棒材制备纳米结构钛镍合金
成熟度:通过小试
技术类型:-
应用行业:制造业
技术简介
项目简介:FIELD: metallurgy.SUBSTANCE: proposed alloy features structure of nanocrystalline grains of B2-phase whereinvolume fraction of 0,1 mcm-size grains and those of shape factor of 2 in mutually perpendicular planes makes at least 90 %. Over 50 % of grains have large angular boundaries misaligned relative to adjacent grains through 15 to 90 degrees. Method of making the bar from said alloy comprises thermomechanical processing including plastic straining and recovery annealing. Intensive plastic straining is made in two steps. At first step, equal-channel angular pressing is made to accumulated strain e≥4. At second step, forge ironing and/or drawing are made. Annealing is carried out either in process and/or after every straining step. Equal-channel angular pressing is performed at 400°C. Forge drawing and ironing are made to total reduction of over 60 % at gradual decrease of temperature to t=450…200 °C, while annealing is performed at t=400…200 °C. EFFECT: higher mechanical and functional properties.项目核心创新点:项目详细用途:预期效益说明:
一种钛镍合金添加少量铝钒均匀布料方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种钛镍合金添加少量铝钒均匀布料方法,冷速大于0.5℃/s时,冷速对全脱碳层深度影响不大,但冷速决定全脱碳层的形貌;冷速较大(5℃/s)的全脱碳层铁素体为等轴铁素体,这些铁素体之间镶嵌着点状的珠光体;而冷速较小(0.5℃/s)的全脱碳层铁素体为长条状,且其生长方向为垂直表面,铁素体之间没有点状的珠光体。在高温段保温一段时间的情况下,α+γ两相区加热对全脱碳层深度的影响很小;在高温段不保温的情况下,α+γ两相区加热产生的全脱碳层会遗留到试样的最终表面,适用于钛镍合金添加少量铝钒均匀布料。
一种钕铁硼磁体离子液体电镀锌镍合金的方法
成熟度:正在研发
技术类型:-
应用行业:制造业
技术简介
一种钕铁硼磁体离子液体电镀锌镍合金的方法是将经镀前处理的钕铁硼磁体作为阴极,锌为阳极,含添加剂的离子液体作为电镀液,在磁力搅拌条件下,控制温度、电流密度和电镀时间对钕铁硼磁体实施电镀锌镍合金工艺,后进行出光、钝化和老化处理。此方法镀液成本低、合成简单、操作温度低,避免了析氢反应,得到的镀层光亮致密,经镀后钝化处理镀层与基体结合牢固,耐腐蚀性好。
一种采用铑镀层的铜表面镀层结构
成熟度:正在研发
技术类型:实用新型
应用行业:制造业
技术简介
本实用新型所述一种采用铑镀层的铜表面镀层结构,包括自下而上设置的铜表面层、预镀镍层、光亮电镀镍层、钯镍合金镀层和铑镀层。预镀镍层与铜表面层相接触,并且预镀镍层位于铜表面层的外侧;光亮电镀镍层与预镀镍层相接触,并且光亮电镀镍层位于预镀镍层的外侧;钯镍合金镀层与光亮电镀镍层相接触,并且钯镍镀层位于光亮电镀镍层的外侧;铑镀层与钯镍合金镀层相接触,并且铑镀层位于钯镍合金镀层的外侧。本实用新型所述一种采用铑镀层的铜表面镀层结构,对铜进行铑电镀可以大大提高镀层的硬度和耐磨性,并赋予铜表面层银白色金属光泽,扩展了铜材质的应用范围。
钇的选择性显色剂对硝基偶氮氯膦在镍合金分析中的应用
成熟度:-
技术类型:-
应用行业:科学研究和技术服务业
技术简介
新型测温材料镍铬-镍硅热电偶和镍基汽车火花塞材料是测温仪表和汽车发动机用的关键材料,其中加入轻稀土元素和钇则可大大提高材料抗氧化性及改善材料的性能。但由于轻稀土和钇的化学性质极为相似,其不经分离直接测定是分析化学领域中长期未解决的问题。该校研制的新稀土显色剂-对硝基偶氮氯膦试剂与钇特征β型反应解决了镍合金中钇和铈组共存时钇的测定问题。这一技术为解决镍、铬热电偶代替昂贵的铂铑热电偶创造了条件。该项成果还可扩大应用于高温合金、钢铁、稀土矿石及钢合金等材料中钇和铈组元素的测定。
高钼、钴、镍合金的综合回收
成熟度:-
技术类型:-
应用行业:制造业
技术简介
该成果是利用该所现有设备,在大量试验的基础上研制的。工艺的关键:试料采用一次氧化焙烧,二次苏打焙烧的生产流程,有效地解决了钼与钴、镍的分离。通过控制最佳工艺条件,不仅有价的回收率高,而且产品质量稳定,生产成本低,产品可全部出口,市场前景乐观。该工艺流程短,设备少,环保措施完善,具有明显的经济效益和社会效益。
一种用于锰钒镍合金钢的正火工艺
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种用于锰钒镍合金钢的正火工艺,属于金属热处理技术领域。将根据钢板的厚度进行分组,不同组别的钢板,采用不同的正火工艺,从而使得不同厚度钢板的强度均能满足标准要求。该钢种成分为C≤0.20%,Mn≤1.70%,Si=0.10%~0.50%,V=0.10%~0.18%,Ni=0.40%~0.70%,P≤0.035%,S≤0.035%,其余为Fe和不可避免残余元素。将厚度≤75mm的钢板分为五组,根据不同的分组,采用不同的正火温度和不同的在炉时间。优点在于,工艺简单易行;不同厚度的钢板,其强度均满足标准要求,同时可以避免不必要的能源浪费。
一种镍合金200um涂层的制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
摘要:本发明公开了一种镍合金200um涂层的制备方法,首先对工件表面进行热处理,然后取各种金属粉按比例配置合金粉并搅拌均匀,最后采用等离子喷涂的方法在工件表面喷涂一层合金层。其优点在于:方法简单,原料易得,综合性能好,应用广泛。
一种镍合金基体表面热障涂层及制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种镍合金基体表面热障涂层(专利号201110347751.7),包括微晶玻璃粘结层和陶瓷表层,所述微晶玻璃粘结层及所述陶瓷表层分别由微晶玻璃粉末及稀土锆酸盐粉末通过料浆喷涂沉积在镍合金基体表面。本发明采用与基体有着良好结合的微晶玻璃作为粘结层,可有效提高涂层的抗热震性能;以稀土锆酸盐为表层材料,使涂层具有更好的隔热和抗氧化性能。通过调整料浆喷涂工艺参数可以方便的调整涂层的厚度,以使涂层的强度与厚度达到良好的比例,适应不同的服役环境条件。本发明工艺方法简单,操作简便,制备的涂层具有良好的抗热震性能、隔热和抗氧化性能,可大幅降低生产成本,适用于现代航空发动机、航天器和火箭发动机以及舰艇和工业燃气轮机的关键热端部件的表面处理。
一种铜粉表面包覆磷镍合金层的超声化学制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
本发明涉及金属包覆型复合粉末,特指一种铜粉表面包覆磷镍合金层的超声化学制备方法。该方法的特点是在传统化学镀的工艺中有效的加入了高能超声搅拌,利用其的空穴效应、震荡等效应,提高了镍包覆铜复合粉末制备效率,解决了粉末团聚等问题。另外本发明在制备镍磷包覆型铜粉时,使用次亚磷酸钠作还原剂的酸性化学镀镀液,镀液配制简单,稳定性强,镀覆前的铜粉使用盐酸进行活化处理,克服了传统的铜粉表面要经过贵金属盐活化敏化处理时贵金属钯盐带入镀液导致镀液分解的问题,又简化了粉末的活化工序,同时在整个镀覆的过程中保持高能超声搅拌,制得的复合粉末分散性极好,包覆层完整均匀,镀层致密,呈非晶态。
找到19项技术成果数据。
找技术 >通过形状记忆棒材制备纳米结构钛镍合金
成熟度:通过小试
技术类型:-
应用行业:制造业
技术简介
项目简介:FIELD: metallurgy.SUBSTANCE: proposed alloy features structure of nanocrystalline grains of B2-phase whereinvolume fraction of 0,1 mcm-size grains and those of shape factor of 2 in mutually perpendicular planes makes at least 90 %. Over 50 % of grains have large angular boundaries misaligned relative to adjacent grains through 15 to 90 degrees. Method of making the bar from said alloy comprises thermomechanical processing including plastic straining and recovery annealing. Intensive plastic straining is made in two steps. At first step, equal-channel angular pressing is made to accumulated strain e≥4. At second step, forge ironing and/or drawing are made. Annealing is carried out either in process and/or after every straining step. Equal-channel angular pressing is performed at 400°C. Forge drawing and ironing are made to total reduction of over 60 % at gradual decrease of temperature to t=450…200 °C, while annealing is performed at t=400…200 °C. EFFECT: higher mechanical and functional properties.项目核心创新点:项目详细用途:预期效益说明:
一种钛镍合金添加少量铝钒均匀布料方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种钛镍合金添加少量铝钒均匀布料方法,冷速大于0.5℃/s时,冷速对全脱碳层深度影响不大,但冷速决定全脱碳层的形貌;冷速较大(5℃/s)的全脱碳层铁素体为等轴铁素体,这些铁素体之间镶嵌着点状的珠光体;而冷速较小(0.5℃/s)的全脱碳层铁素体为长条状,且其生长方向为垂直表面,铁素体之间没有点状的珠光体。在高温段保温一段时间的情况下,α+γ两相区加热对全脱碳层深度的影响很小;在高温段不保温的情况下,α+γ两相区加热产生的全脱碳层会遗留到试样的最终表面,适用于钛镍合金添加少量铝钒均匀布料。
一种钕铁硼磁体离子液体电镀锌镍合金的方法
成熟度:正在研发
技术类型:-
应用行业:制造业
技术简介
一种钕铁硼磁体离子液体电镀锌镍合金的方法是将经镀前处理的钕铁硼磁体作为阴极,锌为阳极,含添加剂的离子液体作为电镀液,在磁力搅拌条件下,控制温度、电流密度和电镀时间对钕铁硼磁体实施电镀锌镍合金工艺,后进行出光、钝化和老化处理。此方法镀液成本低、合成简单、操作温度低,避免了析氢反应,得到的镀层光亮致密,经镀后钝化处理镀层与基体结合牢固,耐腐蚀性好。
一种采用铑镀层的铜表面镀层结构
成熟度:正在研发
技术类型:实用新型
应用行业:制造业
技术简介
本实用新型所述一种采用铑镀层的铜表面镀层结构,包括自下而上设置的铜表面层、预镀镍层、光亮电镀镍层、钯镍合金镀层和铑镀层。预镀镍层与铜表面层相接触,并且预镀镍层位于铜表面层的外侧;光亮电镀镍层与预镀镍层相接触,并且光亮电镀镍层位于预镀镍层的外侧;钯镍合金镀层与光亮电镀镍层相接触,并且钯镍镀层位于光亮电镀镍层的外侧;铑镀层与钯镍合金镀层相接触,并且铑镀层位于钯镍合金镀层的外侧。本实用新型所述一种采用铑镀层的铜表面镀层结构,对铜进行铑电镀可以大大提高镀层的硬度和耐磨性,并赋予铜表面层银白色金属光泽,扩展了铜材质的应用范围。
钇的选择性显色剂对硝基偶氮氯膦在镍合金分析中的应用
成熟度:-
技术类型:-
应用行业:科学研究和技术服务业
技术简介
新型测温材料镍铬-镍硅热电偶和镍基汽车火花塞材料是测温仪表和汽车发动机用的关键材料,其中加入轻稀土元素和钇则可大大提高材料抗氧化性及改善材料的性能。但由于轻稀土和钇的化学性质极为相似,其不经分离直接测定是分析化学领域中长期未解决的问题。该校研制的新稀土显色剂-对硝基偶氮氯膦试剂与钇特征β型反应解决了镍合金中钇和铈组共存时钇的测定问题。这一技术为解决镍、铬热电偶代替昂贵的铂铑热电偶创造了条件。该项成果还可扩大应用于高温合金、钢铁、稀土矿石及钢合金等材料中钇和铈组元素的测定。
高钼、钴、镍合金的综合回收
成熟度:-
技术类型:-
应用行业:制造业
技术简介
该成果是利用该所现有设备,在大量试验的基础上研制的。工艺的关键:试料采用一次氧化焙烧,二次苏打焙烧的生产流程,有效地解决了钼与钴、镍的分离。通过控制最佳工艺条件,不仅有价的回收率高,而且产品质量稳定,生产成本低,产品可全部出口,市场前景乐观。该工艺流程短,设备少,环保措施完善,具有明显的经济效益和社会效益。
一种用于锰钒镍合金钢的正火工艺
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种用于锰钒镍合金钢的正火工艺,属于金属热处理技术领域。将根据钢板的厚度进行分组,不同组别的钢板,采用不同的正火工艺,从而使得不同厚度钢板的强度均能满足标准要求。该钢种成分为C≤0.20%,Mn≤1.70%,Si=0.10%~0.50%,V=0.10%~0.18%,Ni=0.40%~0.70%,P≤0.035%,S≤0.035%,其余为Fe和不可避免残余元素。将厚度≤75mm的钢板分为五组,根据不同的分组,采用不同的正火温度和不同的在炉时间。优点在于,工艺简单易行;不同厚度的钢板,其强度均满足标准要求,同时可以避免不必要的能源浪费。
一种镍合金200um涂层的制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
摘要:本发明公开了一种镍合金200um涂层的制备方法,首先对工件表面进行热处理,然后取各种金属粉按比例配置合金粉并搅拌均匀,最后采用等离子喷涂的方法在工件表面喷涂一层合金层。其优点在于:方法简单,原料易得,综合性能好,应用广泛。
一种镍合金基体表面热障涂层及制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种镍合金基体表面热障涂层(专利号201110347751.7),包括微晶玻璃粘结层和陶瓷表层,所述微晶玻璃粘结层及所述陶瓷表层分别由微晶玻璃粉末及稀土锆酸盐粉末通过料浆喷涂沉积在镍合金基体表面。本发明采用与基体有着良好结合的微晶玻璃作为粘结层,可有效提高涂层的抗热震性能;以稀土锆酸盐为表层材料,使涂层具有更好的隔热和抗氧化性能。通过调整料浆喷涂工艺参数可以方便的调整涂层的厚度,以使涂层的强度与厚度达到良好的比例,适应不同的服役环境条件。本发明工艺方法简单,操作简便,制备的涂层具有良好的抗热震性能、隔热和抗氧化性能,可大幅降低生产成本,适用于现代航空发动机、航天器和火箭发动机以及舰艇和工业燃气轮机的关键热端部件的表面处理。
一种铜粉表面包覆磷镍合金层的超声化学制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
本发明涉及金属包覆型复合粉末,特指一种铜粉表面包覆磷镍合金层的超声化学制备方法。该方法的特点是在传统化学镀的工艺中有效的加入了高能超声搅拌,利用其的空穴效应、震荡等效应,提高了镍包覆铜复合粉末制备效率,解决了粉末团聚等问题。另外本发明在制备镍磷包覆型铜粉时,使用次亚磷酸钠作还原剂的酸性化学镀镀液,镀液配制简单,稳定性强,镀覆前的铜粉使用盐酸进行活化处理,克服了传统的铜粉表面要经过贵金属盐活化敏化处理时贵金属钯盐带入镀液导致镀液分解的问题,又简化了粉末的活化工序,同时在整个镀覆的过程中保持高能超声搅拌,制得的复合粉末分散性极好,包覆层完整均匀,镀层致密,呈非晶态。
找到19项技术成果数据。
找技术 >通过形状记忆棒材制备纳米结构钛镍合金
成熟度:通过小试
技术类型:-
应用行业:制造业
技术简介
项目简介:FIELD: metallurgy.SUBSTANCE: proposed alloy features structure of nanocrystalline grains of B2-phase whereinvolume fraction of 0,1 mcm-size grains and those of shape factor of 2 in mutually perpendicular planes makes at least 90 %. Over 50 % of grains have large angular boundaries misaligned relative to adjacent grains through 15 to 90 degrees. Method of making the bar from said alloy comprises thermomechanical processing including plastic straining and recovery annealing. Intensive plastic straining is made in two steps. At first step, equal-channel angular pressing is made to accumulated strain e≥4. At second step, forge ironing and/or drawing are made. Annealing is carried out either in process and/or after every straining step. Equal-channel angular pressing is performed at 400°C. Forge drawing and ironing are made to total reduction of over 60 % at gradual decrease of temperature to t=450…200 °C, while annealing is performed at t=400…200 °C. EFFECT: higher mechanical and functional properties.项目核心创新点:项目详细用途:预期效益说明:
一种钛镍合金添加少量铝钒均匀布料方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种钛镍合金添加少量铝钒均匀布料方法,冷速大于0.5℃/s时,冷速对全脱碳层深度影响不大,但冷速决定全脱碳层的形貌;冷速较大(5℃/s)的全脱碳层铁素体为等轴铁素体,这些铁素体之间镶嵌着点状的珠光体;而冷速较小(0.5℃/s)的全脱碳层铁素体为长条状,且其生长方向为垂直表面,铁素体之间没有点状的珠光体。在高温段保温一段时间的情况下,α+γ两相区加热对全脱碳层深度的影响很小;在高温段不保温的情况下,α+γ两相区加热产生的全脱碳层会遗留到试样的最终表面,适用于钛镍合金添加少量铝钒均匀布料。
一种钕铁硼磁体离子液体电镀锌镍合金的方法
成熟度:正在研发
技术类型:-
应用行业:制造业
技术简介
一种钕铁硼磁体离子液体电镀锌镍合金的方法是将经镀前处理的钕铁硼磁体作为阴极,锌为阳极,含添加剂的离子液体作为电镀液,在磁力搅拌条件下,控制温度、电流密度和电镀时间对钕铁硼磁体实施电镀锌镍合金工艺,后进行出光、钝化和老化处理。此方法镀液成本低、合成简单、操作温度低,避免了析氢反应,得到的镀层光亮致密,经镀后钝化处理镀层与基体结合牢固,耐腐蚀性好。
一种采用铑镀层的铜表面镀层结构
成熟度:正在研发
技术类型:实用新型
应用行业:制造业
技术简介
本实用新型所述一种采用铑镀层的铜表面镀层结构,包括自下而上设置的铜表面层、预镀镍层、光亮电镀镍层、钯镍合金镀层和铑镀层。预镀镍层与铜表面层相接触,并且预镀镍层位于铜表面层的外侧;光亮电镀镍层与预镀镍层相接触,并且光亮电镀镍层位于预镀镍层的外侧;钯镍合金镀层与光亮电镀镍层相接触,并且钯镍镀层位于光亮电镀镍层的外侧;铑镀层与钯镍合金镀层相接触,并且铑镀层位于钯镍合金镀层的外侧。本实用新型所述一种采用铑镀层的铜表面镀层结构,对铜进行铑电镀可以大大提高镀层的硬度和耐磨性,并赋予铜表面层银白色金属光泽,扩展了铜材质的应用范围。
钇的选择性显色剂对硝基偶氮氯膦在镍合金分析中的应用
成熟度:-
技术类型:-
应用行业:科学研究和技术服务业
技术简介
新型测温材料镍铬-镍硅热电偶和镍基汽车火花塞材料是测温仪表和汽车发动机用的关键材料,其中加入轻稀土元素和钇则可大大提高材料抗氧化性及改善材料的性能。但由于轻稀土和钇的化学性质极为相似,其不经分离直接测定是分析化学领域中长期未解决的问题。该校研制的新稀土显色剂-对硝基偶氮氯膦试剂与钇特征β型反应解决了镍合金中钇和铈组共存时钇的测定问题。这一技术为解决镍、铬热电偶代替昂贵的铂铑热电偶创造了条件。该项成果还可扩大应用于高温合金、钢铁、稀土矿石及钢合金等材料中钇和铈组元素的测定。
高钼、钴、镍合金的综合回收
成熟度:-
技术类型:-
应用行业:制造业
技术简介
该成果是利用该所现有设备,在大量试验的基础上研制的。工艺的关键:试料采用一次氧化焙烧,二次苏打焙烧的生产流程,有效地解决了钼与钴、镍的分离。通过控制最佳工艺条件,不仅有价的回收率高,而且产品质量稳定,生产成本低,产品可全部出口,市场前景乐观。该工艺流程短,设备少,环保措施完善,具有明显的经济效益和社会效益。
一种用于锰钒镍合金钢的正火工艺
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种用于锰钒镍合金钢的正火工艺,属于金属热处理技术领域。将根据钢板的厚度进行分组,不同组别的钢板,采用不同的正火工艺,从而使得不同厚度钢板的强度均能满足标准要求。该钢种成分为C≤0.20%,Mn≤1.70%,Si=0.10%~0.50%,V=0.10%~0.18%,Ni=0.40%~0.70%,P≤0.035%,S≤0.035%,其余为Fe和不可避免残余元素。将厚度≤75mm的钢板分为五组,根据不同的分组,采用不同的正火温度和不同的在炉时间。优点在于,工艺简单易行;不同厚度的钢板,其强度均满足标准要求,同时可以避免不必要的能源浪费。
一种镍合金200um涂层的制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
摘要:本发明公开了一种镍合金200um涂层的制备方法,首先对工件表面进行热处理,然后取各种金属粉按比例配置合金粉并搅拌均匀,最后采用等离子喷涂的方法在工件表面喷涂一层合金层。其优点在于:方法简单,原料易得,综合性能好,应用广泛。
一种镍合金基体表面热障涂层及制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种镍合金基体表面热障涂层(专利号201110347751.7),包括微晶玻璃粘结层和陶瓷表层,所述微晶玻璃粘结层及所述陶瓷表层分别由微晶玻璃粉末及稀土锆酸盐粉末通过料浆喷涂沉积在镍合金基体表面。本发明采用与基体有着良好结合的微晶玻璃作为粘结层,可有效提高涂层的抗热震性能;以稀土锆酸盐为表层材料,使涂层具有更好的隔热和抗氧化性能。通过调整料浆喷涂工艺参数可以方便的调整涂层的厚度,以使涂层的强度与厚度达到良好的比例,适应不同的服役环境条件。本发明工艺方法简单,操作简便,制备的涂层具有良好的抗热震性能、隔热和抗氧化性能,可大幅降低生产成本,适用于现代航空发动机、航天器和火箭发动机以及舰艇和工业燃气轮机的关键热端部件的表面处理。
一种铜粉表面包覆磷镍合金层的超声化学制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
本发明涉及金属包覆型复合粉末,特指一种铜粉表面包覆磷镍合金层的超声化学制备方法。该方法的特点是在传统化学镀的工艺中有效的加入了高能超声搅拌,利用其的空穴效应、震荡等效应,提高了镍包覆铜复合粉末制备效率,解决了粉末团聚等问题。另外本发明在制备镍磷包覆型铜粉时,使用次亚磷酸钠作还原剂的酸性化学镀镀液,镀液配制简单,稳定性强,镀覆前的铜粉使用盐酸进行活化处理,克服了传统的铜粉表面要经过贵金属盐活化敏化处理时贵金属钯盐带入镀液导致镀液分解的问题,又简化了粉末的活化工序,同时在整个镀覆的过程中保持高能超声搅拌,制得的复合粉末分散性极好,包覆层完整均匀,镀层致密,呈非晶态。
找到19项技术成果数据。
找技术 >通过形状记忆棒材制备纳米结构钛镍合金
成熟度:通过小试
技术类型:-
应用行业:制造业
技术简介
项目简介:FIELD: metallurgy.SUBSTANCE: proposed alloy features structure of nanocrystalline grains of B2-phase whereinvolume fraction of 0,1 mcm-size grains and those of shape factor of 2 in mutually perpendicular planes makes at least 90 %. Over 50 % of grains have large angular boundaries misaligned relative to adjacent grains through 15 to 90 degrees. Method of making the bar from said alloy comprises thermomechanical processing including plastic straining and recovery annealing. Intensive plastic straining is made in two steps. At first step, equal-channel angular pressing is made to accumulated strain e≥4. At second step, forge ironing and/or drawing are made. Annealing is carried out either in process and/or after every straining step. Equal-channel angular pressing is performed at 400°C. Forge drawing and ironing are made to total reduction of over 60 % at gradual decrease of temperature to t=450…200 °C, while annealing is performed at t=400…200 °C. EFFECT: higher mechanical and functional properties.项目核心创新点:项目详细用途:预期效益说明:
一种钛镍合金添加少量铝钒均匀布料方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种钛镍合金添加少量铝钒均匀布料方法,冷速大于0.5℃/s时,冷速对全脱碳层深度影响不大,但冷速决定全脱碳层的形貌;冷速较大(5℃/s)的全脱碳层铁素体为等轴铁素体,这些铁素体之间镶嵌着点状的珠光体;而冷速较小(0.5℃/s)的全脱碳层铁素体为长条状,且其生长方向为垂直表面,铁素体之间没有点状的珠光体。在高温段保温一段时间的情况下,α+γ两相区加热对全脱碳层深度的影响很小;在高温段不保温的情况下,α+γ两相区加热产生的全脱碳层会遗留到试样的最终表面,适用于钛镍合金添加少量铝钒均匀布料。
一种钕铁硼磁体离子液体电镀锌镍合金的方法
成熟度:正在研发
技术类型:-
应用行业:制造业
技术简介
一种钕铁硼磁体离子液体电镀锌镍合金的方法是将经镀前处理的钕铁硼磁体作为阴极,锌为阳极,含添加剂的离子液体作为电镀液,在磁力搅拌条件下,控制温度、电流密度和电镀时间对钕铁硼磁体实施电镀锌镍合金工艺,后进行出光、钝化和老化处理。此方法镀液成本低、合成简单、操作温度低,避免了析氢反应,得到的镀层光亮致密,经镀后钝化处理镀层与基体结合牢固,耐腐蚀性好。
一种采用铑镀层的铜表面镀层结构
成熟度:正在研发
技术类型:实用新型
应用行业:制造业
技术简介
本实用新型所述一种采用铑镀层的铜表面镀层结构,包括自下而上设置的铜表面层、预镀镍层、光亮电镀镍层、钯镍合金镀层和铑镀层。预镀镍层与铜表面层相接触,并且预镀镍层位于铜表面层的外侧;光亮电镀镍层与预镀镍层相接触,并且光亮电镀镍层位于预镀镍层的外侧;钯镍合金镀层与光亮电镀镍层相接触,并且钯镍镀层位于光亮电镀镍层的外侧;铑镀层与钯镍合金镀层相接触,并且铑镀层位于钯镍合金镀层的外侧。本实用新型所述一种采用铑镀层的铜表面镀层结构,对铜进行铑电镀可以大大提高镀层的硬度和耐磨性,并赋予铜表面层银白色金属光泽,扩展了铜材质的应用范围。
钇的选择性显色剂对硝基偶氮氯膦在镍合金分析中的应用
成熟度:-
技术类型:-
应用行业:科学研究和技术服务业
技术简介
新型测温材料镍铬-镍硅热电偶和镍基汽车火花塞材料是测温仪表和汽车发动机用的关键材料,其中加入轻稀土元素和钇则可大大提高材料抗氧化性及改善材料的性能。但由于轻稀土和钇的化学性质极为相似,其不经分离直接测定是分析化学领域中长期未解决的问题。该校研制的新稀土显色剂-对硝基偶氮氯膦试剂与钇特征β型反应解决了镍合金中钇和铈组共存时钇的测定问题。这一技术为解决镍、铬热电偶代替昂贵的铂铑热电偶创造了条件。该项成果还可扩大应用于高温合金、钢铁、稀土矿石及钢合金等材料中钇和铈组元素的测定。
高钼、钴、镍合金的综合回收
成熟度:-
技术类型:-
应用行业:制造业
技术简介
该成果是利用该所现有设备,在大量试验的基础上研制的。工艺的关键:试料采用一次氧化焙烧,二次苏打焙烧的生产流程,有效地解决了钼与钴、镍的分离。通过控制最佳工艺条件,不仅有价的回收率高,而且产品质量稳定,生产成本低,产品可全部出口,市场前景乐观。该工艺流程短,设备少,环保措施完善,具有明显的经济效益和社会效益。
一种用于锰钒镍合金钢的正火工艺
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种用于锰钒镍合金钢的正火工艺,属于金属热处理技术领域。将根据钢板的厚度进行分组,不同组别的钢板,采用不同的正火工艺,从而使得不同厚度钢板的强度均能满足标准要求。该钢种成分为C≤0.20%,Mn≤1.70%,Si=0.10%~0.50%,V=0.10%~0.18%,Ni=0.40%~0.70%,P≤0.035%,S≤0.035%,其余为Fe和不可避免残余元素。将厚度≤75mm的钢板分为五组,根据不同的分组,采用不同的正火温度和不同的在炉时间。优点在于,工艺简单易行;不同厚度的钢板,其强度均满足标准要求,同时可以避免不必要的能源浪费。
一种镍合金200um涂层的制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
摘要:本发明公开了一种镍合金200um涂层的制备方法,首先对工件表面进行热处理,然后取各种金属粉按比例配置合金粉并搅拌均匀,最后采用等离子喷涂的方法在工件表面喷涂一层合金层。其优点在于:方法简单,原料易得,综合性能好,应用广泛。
一种镍合金基体表面热障涂层及制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
一种镍合金基体表面热障涂层(专利号201110347751.7),包括微晶玻璃粘结层和陶瓷表层,所述微晶玻璃粘结层及所述陶瓷表层分别由微晶玻璃粉末及稀土锆酸盐粉末通过料浆喷涂沉积在镍合金基体表面。本发明采用与基体有着良好结合的微晶玻璃作为粘结层,可有效提高涂层的抗热震性能;以稀土锆酸盐为表层材料,使涂层具有更好的隔热和抗氧化性能。通过调整料浆喷涂工艺参数可以方便的调整涂层的厚度,以使涂层的强度与厚度达到良好的比例,适应不同的服役环境条件。本发明工艺方法简单,操作简便,制备的涂层具有良好的抗热震性能、隔热和抗氧化性能,可大幅降低生产成本,适用于现代航空发动机、航天器和火箭发动机以及舰艇和工业燃气轮机的关键热端部件的表面处理。
一种铜粉表面包覆磷镍合金层的超声化学制备方法
成熟度:正在研发
技术类型:发明
应用行业:制造业
技术简介
本发明涉及金属包覆型复合粉末,特指一种铜粉表面包覆磷镍合金层的超声化学制备方法。该方法的特点是在传统化学镀的工艺中有效的加入了高能超声搅拌,利用其的空穴效应、震荡等效应,提高了镍包覆铜复合粉末制备效率,解决了粉末团聚等问题。另外本发明在制备镍磷包覆型铜粉时,使用次亚磷酸钠作还原剂的酸性化学镀镀液,镀液配制简单,稳定性强,镀覆前的铜粉使用盐酸进行活化处理,克服了传统的铜粉表面要经过贵金属盐活化敏化处理时贵金属钯盐带入镀液导致镀液分解的问题,又简化了粉末的活化工序,同时在整个镀覆的过程中保持高能超声搅拌,制得的复合粉末分散性极好,包覆层完整均匀,镀层致密,呈非晶态。